Studies on the Structure and Catalytic Properties for Heck Reaction of Troxerutin Supported Palladium Catalyst

Theoretical Foundations of Chemical Engineering - Troxerutin supported palladium (TXT-Pd) catalyst was prepared readily by using one-step synthetic method. As-fabricated TXT-Pd catalyst was...     

Fermented and malted millet products in Africa: Expedition from traditional/ethnic foods to industrial value-added products

With the prevalent food insecurity in Africa, there is a growing need to utilize the available crops to develop nutritious, affordable and palatable food for the populace. Millet is critical in this role, relative to its abundance in the continent and good nutritional composition. For ages, fermentation and malting have been traditionally used to transform millet into variety of produce. A paradigm shift has however occurred over the years, giving birth to new commercially available products. This review thus appraises and gives an overview of traditional and modern fermented and malted products. Although, millet has been diversified to several products, its major food uses are still restrained to traditional consumers and largely remains underutilized. Considering the potential embedded in this grain, it is important to explore this crop through the application of appropriate modern fermentation and malting technologies. This will ensure the availability of ready to eat (RTE) and ready to use (RTU) food products and to a large extent address the incessant food security challenges plaguing Africa.     

Transformation of sputtered calcium copper titanate thin film into nanorods by sequential annealing

Rapid synthesis of long calcium copper titanate (CCTO) nanorods was carried out by sequential annealing. CCTO thin films have been deposited on p-Si substrate by RF sputtering technique and afterwards, the samples were thermally treated using a preheated furnace by varying the annealing temperature from 850 °C to 1100 °C. CCTO nanorods of 12 µm lengths and 400–600 nm diameters were synthesized at 1100 °C. Based on the FESEM observations, a plausible growth mechanism has been proposed to explain the formation of nanorods. The (220) XRD peak of the CCTO film became prominent for the annealing temperature of 950 °C. The presence of nanoscale crystals in amorphous matrix has been observed by HRTEM studies. The elemental mapping of CCTO nanorod has shown a spatial variation of elements throughout the nanorod. The oxide and interface charge density was found to be increased with the rise in annealing temperature.     

Gellan gum–O,O′‐bis(2‐aminopropyl)‐polyethylene glycol hydrogel for controlled fertilizer release

A gellan gum–Jeffamine superabsorbent hydrogel was obtained with different crosslink densities using different amounts of (1‐ethyl‐3‐(3‐dimethylaminopropyl)carbodiimide hydrochloride) and N‐hydroxysuccinimide. Infrared spectroscopy and thermal analysis confirm the crosslinking. A morphology analysis indicates denser structures for samples with higher crosslinking points. The swelling degree in high‐acyl gellan gum hydrogels was equivalent to 145 times their dry weight, and 77 times when low‐acyl gellan gum was used. Hydrogels also showed a 450 min water retention, as opposed to 280 min for pure water, evidencing good humidity control, suitable for use in arid climates. They also demonstrated a maximum release of commercial fertilizer of about 400 mg per gram for KH₂PO₄ and about 300 mg per gram for NPK 20‐5‐20. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 45636.     

Large scale cathodic exfoliation of graphite using deep eutectic solvent and water mixture

A short-time and low-cost synthesis route was used to produce large lateral size (from 2 to 15 μm) from monolayers to few layers of graphene by a two-step process of electrochemical exfoliation with a deep eutectic solvent in a mixture with water that can be reused, and ultrasonic bath. The graphene was characterized by SEM, TEM, AFM, Raman and electrochemical activity. During the electrochemical exfoliation, high expanded graphene particles were obtained and these were dispersed in a mixture of water with 5%wt ethylene glycol by an ultrasonic bath in order to complete the exfoliation process. An enhancement of the electrical conductivity of these dispersions was obtained with the increase of graphene concentration, 0.38 mg/mL, which best result was achieved with 30 wt% water and a DC voltage of 10 V. It was possible to add a conductive layer to a glass substrate with the graphene obtained and Tyndall effect was observed.